10.5878/e0r5-d487
Karlsson, Stefan
Stefan
Karlsson
0000-0003-2160-6979
RISE Research Institutes of Sweden
Dataset: Viscosity of alumina doped soda lime silicate glasses
Dataset: Viskositet för aluminiumoxid-dopade soda kalk silikatglas
RISE Research Institutes of Sweden
2021
Thermal Properties
Thermal Properties
glass
glas
glass industry
glasindustri
melting
smältning
thermodynamics
termidynamik
viscosity
viskositet
Sensor Characteristics
Sensor Characteristics
Spectral/Engineering
Spectral/Engineering
Earth Science
Earth Science
Science Keywords
Science Keywords
Geophysics
Geofysik
Geochemistry
Geokemi
Materials Engineering
Materialteknik
Mineral and Mine Engineering
Mineral- och gruvteknik
Geoscientific Information
Geovetenskap
Engineering and Technology
Teknik
Earth and Related Environmental Sciences
Geovetenskap och miljövetenskap
Environmental Engineering
Naturresursteknik
Natural Sciences
Naturvetenskap
2021-09-10
2019/2021-08-24
eng
10.5878/4zpb-d632
urn:nbn:se:ri:diva-56387
10.1016/j.jnoncrysol.2021.121149
160.05 KiB
1
Creative Commons Attribution 4.0 International (CC BY 4.0)
Adding alumina to the conventional soda lime silicate glass composition improves many properties, however, also increases the viscosity. Alumina doping of soda lime silicate glasses is investigated and its implications to high temperature viscosity as SiO2 is replaced by Al2O3.
Att tillsätta aluminiumoxid till den konventionella soda -kalk -silikatglaskompositionen förbättrar många egenskaper, men ökar också viskositeten. Aluminiumdopning av soda kalk silikatglas undersöks och dess konsekvenser för högtemperaturviskositet då SiO2 ersätts av Al2O3.
FORMAS
https://ror.org/03pjs1y45
2018‐00707
Tunnare och starkare glas för hållbar produktion och konsumtion